Polyester Resin 1Kg For Vaku 80 Repairs

Description

Laminating resin for the repair of larger holes and damage to GFRP components with fiberglass and fabric reinforcements
• Balanced resin mix
• Excellent application properties
• Special lid/outlet combination
• Easy to use
• Easy to empty down to the last drop

INDICATIONS:
During lamination with glass fiber reinforcement VAKU 90, check that the application is bubble-free.
Apply VAKU 80 "wet on wet" in several passes.
Maximum permitted VOC content for VAKU 80 : 250 g/l for product category 2(b). Maximum VOC content according to the German Ordinance on Solvent-Based Varnishes and Paints (ChemVOC FarbV): 0 g/l
The instructions for use are recommendations based on the tests we have carried out and our experience; perform appropriate tests before each application. Due to the large number of possible applications and conditions of storage and use, no responsibility can be accepted for the result of specific applications. To the extent that our free customer service provides technical information or acts as an advisory service, it disclaims any liability, except where the advice or information provided falls within the scope of the specified contractually agreed service or the advisor acts deliberately . We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop the products.

AREA OF APPLICATION:
• Car/cargo:
In vehicle construction, ships, car bodies and chassis for repairing breaking points. For the repair of GFRP components and for the restoration of shape and stability.

• Metal:
Restoration and repair of GFRP components and construction of prototypes and boats.

< p>INSTRUCTIONS:
• The surface must be clean, dry and free from grease.
• Sand the surfaces
• In order to avoid any defects, always check the correct dosage ratio between filler and hardener
• Dosage: 2% of hardener
• Useful time of use
• 10-15 minutes at 20°C
• Drying time
• 60 minutes at 20°C
• Sandpaper
• P 60-80

SPECIFICATIONS:
• Contents: 869.6 ml
• Conditions for VOC concentration: ChemVOCFarb
• Chemical basis: Polyester resin
• Color: Yellowish
• Hardness supplement: 2 %
• Density: 1 ,15 g/cm³
• Max useful life: 15 min
• Min useful life: 10 min
• Conditions for duration: at 20°C
• Conditions for drying time : at 20°C
• Min drying time: 60 min
• Max temperature resistance of hardened material: 80 °C
• Max admissible VOC concentration: 250 g/l
• Storage time: 12 Months